Dissimilar metal weld cracks (between ferritic and austenitic materials) form:

API RP 571 explains the typical location of dissimilar metal weld (DMW) cracks as follows:

“DMW cracking usually occurs in the heat-affected zone (HAZ) on the ferritic side of the weld.”

“The difference in thermal expansion coefficients, grain structures, and creep rates between the ferritic and austenitic materials contributes to the development of high stress and strain concentrations in the HAZ of the ferritic material.”

(Reference: API RP 571, Section 4.2.1.6 – Dissimilar Metal Weld Cracking)

Thus, these cracks do not occur in the center of the weld or on the austenitic side, but rather at the ferritic HAZ, making option A correct.